Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultramid® A3Z HP - PA66-I - BASF

Material Data Center offers the following functions for Ultramid® A3Z HP:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Ultramid A datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
机械性能 - 热性能 - 其它性能
Any use of this information falls under the rules of our disclaimer.
材料文字说明
抗冲击改性且稳定的注塑等级， 用于具有良好的低温抗冲击性零部件和外壳。
机械性能干 / 已调节单位Test Standard
ISO数据
拉伸模量 1900 / 1060 MPa ISO 527
屈服应力 50 / - MPa ISO 527
屈服伸长率 5 / - % ISO 527
名义断裂伸长率 45 / - % ISO 527
无缺口简支梁冲击强度, +23°C N / N kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C N / N kJ/m² ISO 179/1eU
简支梁缺口冲击强度, +23°C 90 / 113 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C 28 / 19 kJ/m² ISO 179/1eA
热性能干 / 已调节单位Test Standard
ISO数据
熔融温度, 10°C/min 262 / * °C ISO 11357-1/-3
热变形温度, 1.80 MPa 64 / * °C ISO 75-1/-2
热变形温度, 0.45 MPa 170 / * °C ISO 75-1/-2
其它性能干 / 已调节单位Test Standard
密度 1070 / - kg/m³ ISO 1183
典型数据
加工方法
注塑
特殊性能
高冲击韧性的/经抗冲改性的
地区供应
北美
其他信息
注塑成型
Max. Water content: 0.20%
Product is supplied in sealed containers and
drying prior to molding is not required. If drying
becomes necessary, a dehumidifying or desiccant dryer
operating at 80 degC (176 degF) is recommended. Drying time is
dependent on moisture level, but 2-4 hours is generally
sufficient.
Further information concerning safe handling procedures
can be obtained from the Material Safety Data Sheet.
Alternatively, please contact your BASF representative.
PROCESSING
Melt Temperature 280-304 degC (536-580 degF)
Mold Temperature 60-100 degC (140-212 degF)
Injection and Packing Pressure 35-125 bar (500-1500 psi)
Back Pressure 0-0.35 MPa (0-50 psi)
Screw Speed 40-80 rpm
Screw Compression Ratio 3:1 to 4:1

This product can be processed over a wide range of mold
temperatures; however, for applications where aesthetics are
critical, a mold surface temperature of 60-100 degC (140-212 degF)
is recommended.

Injection pressure controls the filling of the part and should
be applied for 90% of ram travel. Packing pressure affects
the final part and can be used effectively in controlling
sink marks and shrinkage. It should be applied and maintained
until the gate area is completely frozen off.
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com